Synthesis and Study of some Physical Properties of "Cdo/Nio" Nanocomposite Via Sol-Gel Method and their Antibacterial Activities

المصدر: مجلة جامعة البيضاء
الناشر: جامعة البيضاء
المؤلف الرئيسي: Al-Jezbi, Amatalkareem Mohammed (Author)
المجلد/العدد: مج4, ع2
محكمة: نعم
الدولة: اليمن
التاريخ الميلادي: 2022
الشهر: أغسطس
الصفحات: 998 - 1017
ISSN: 2709-9695
رقم MD: 1330255
نوع المحتوى: بحوث ومقالات
اللغة: الإنجليزية
قواعد المعلومات: EduSearch, HumanIndex
مواضيع:
كلمات المؤلف المفتاحية:
Antibacterial | Oxide Mixed | Optical | Electrical and Cadmium Oxide
رابط المحتوى:
صورة الغلاف QR قانون
حفظ في:
LEADER 02531nam a22002297a 4500
001 2088204
041 |a eng 
044 |b اليمن 
100 |9 705307  |a Al-Jezbi, Amatalkareem Mohammed  |e Author 
245 |a Synthesis and Study of some Physical Properties of "Cdo/Nio" Nanocomposite Via Sol-Gel Method and their Antibacterial Activities 
260 |b جامعة البيضاء  |c 2022  |g أغسطس 
300 |a 998 - 1017 
336 |a بحوث ومقالات  |b Article 
520 |b The NiO and CdO nanoxides as well as the CdO/NiO oxides mixture were prepared in five samples with different concentrations where the ratio of CdO/NiO was [(1: 0), (3: 1), (1: 1), (1: 3), (0: 1)] by using the gel solution using a polyvinyl alcohol solution (PVA) and the samples were platelimbed at (500̊C) for three hours. The structural properties of the prepared oxides resulting from the cracking process were studied. The XRD results show the presence of pure cadmium oxide diffraction patterns in the sample (S1) as well as the pure nickel oxide in the sample (S5) and confirm the presence of the CdO/ NiO oxide mixture in the samples (S2, S3, S4), The results of XRD also show, through calculations, that the specific surface area increases with increasing granular size and decreases with decreasing granular size. XRD calculations also show that the intensity of eruptions decreases as the granular volume increases and increases with decreasing granular size. Optical measurements were taken and absorption spectra at wavelength (215 nm) within the UV range. The results of the optical measurements show an increase in the energy gap of the mixture. Samples were taken for continuous electrical conductivity measurements. It was found that the highest conductivity was the sample (S3) which reached (0.394 S/ cm), and the biological efficacy sensitivity of the samples was tested on six types of bacteria. The samples show varying efficacy on the six types, all of which were highly influencing the samples of the bacteria under study. 
653 |a الخواص الفيزيائية  |a المركبات الكيميائية  |a مضادات البكتيريا 
692 |b Antibacterial  |b Oxide Mixed  |b Optical  |b Electrical and Cadmium Oxide 
773 |c 059  |e AlBayda University Journal  |f Mağallaẗ ğāmiʿaẗ al-Bayḍāʾ li-l-buḥūṯ  |l 002  |m مج4, ع2  |o 2422  |s مجلة جامعة البيضاء  |v 004  |x 2709-9695 
856 |u 2422-004-002-059.pdf 
930 |d y  |p y  |q n 
995 |a EduSearch 
995 |a HumanIndex 
999 |c 1330255  |d 1330255 

عناصر مشابهة